Galvanizing Tank/Galvanized Kettle/Zinc Kettle
Hot dip Galvanizing Tank/Galvanized Kettle/Zinc Kettle is made of special steel sheet XG08, low C, Si, S, P chemical composition,with characteristics of corrosion resistance and long service life.
Product Description
Each year more than 100 galvanizing kettles are produced in our factory. There are almost no restrictions on the dimensions, shapes and weights of the kettle.
In addition to the classic batch galvanizing kettles , you can also get kettles for continuous galvanizing and spin galvanizing.
Our entire production is under design standard, manufacturing and testing standard, from material selecting, forming to welding and testing.
Features of galvanized kettles
The material we use is XG08, which is the best steel sheet for making galvanizing kettle in China, it contains low chemical composition of Carbon, Silicon, Sulphur and Phosphorus to limit the interaction between zinc and iron thereby lowering the wearing rate of the kettle wall, prolong the service life of the kettle.
We do 100% ultrasonic test to the steel sheet XG08 before cutting.
The galvanizing kettle is hydraulically formed at one time, and the U-shaped structure with no horizontal welds.
Do 100% ultrasonic test to each welding line to the kettle to ensure good quality.
It passed the CE certification in 2019.
Process of producing Galvanizing Tank
Steel Sheet Preparing & Ultrasonic detecting -- Cutting -- Annealing -- Forming -- Integrated end -- Middle U shape -- Welding -- Ultrasonic detect -- Inspection -- Delivery
Click to ask for a quote available parameters (customizable parameters)
Use of Galvanized Kettle
Once the steel is completely cleaned, it is ready to be immersed in the Zinc Kettle's zinc bath. Galvanizing kettles contain zinc as specified by ASTM B6, which specifies any of the three types of zinc, each with a minimum purity of 98%. Other metals can sometimes be added to the kettle to promote certain desirable properties of the galvanized coating.
The Galvanizing Tank is heated to a temperature of 820-860 F (438-460 C), at which point the zinc is in a liquid state. The steel is lowered at an angle into the Galvanized Kettle and remains in the plating solution until the steel is heated to the plating temperature. Once the diffusion reaction between iron and zinc is complete, the steel product is removed from the zinc kettle. The entire immersion usually lasts less than ten minutes, depending on the thickness of the steel.
When the steel is removed from the Galvanized Kettle, it may receive a post-treatment to enhance the galvanized coating. One of the most common treatments is quenching. The quench tank contains primarily water, but chemicals may also be added to form a passivation layer that protects the galvanized steel during storage and transportation. Other finishing steps include removing zinc droplets or spikes and grinding them off.
Buy Galvanized Kettle customer reviews
The Galvanizing tanks for Uruguay Client were shipped on Mar.02, 2021. Recently we received feedback from client that the tanks were reached in very good condition, they were very satisfied with the good quality and professional service, gave us very high praise.
These are great encourage to us, we will continue to make good products to meet the demand of more clients.
These hot-dip galvanizing facts may be of interest to you:
What is Hot Dip Galvanizing Equipment?
11 Facts about Hot-Dip Galvanizing
Considerations When Choosing the Appropriate Hot Dip Galvanizing Equipment
How to Achieve Energy Saving of Hot-dip Galvanizing Equipment
Hot-Dip Galvanizing Process in 3 Steps
How does Hot-dip Galvanizing Strengthen Steel?
How We Improve the Hot Dip Galvanizing Process
How Much Is Hot Dip Galvanizing?
How to Control Pollution in A Galvanization Setup?
Knowing Hot Dip Galvanizing and Its Numerous Benefits
PP Storage Tanks VS Stainless Steel Tanks